フッ化バリウム(BaF2)ウェッジウィンドウ
- 30 arcminute Wedge
- Eliminate Etalon Effects and Prevent Cavity Feedback
- Uncoated and AR-Coated BaF2 Substrates
- Custom Options Available
Back Reflections from Wedges are not Collinear with the Incident Beam
(Drawing not to Scale)
WW01050
Ø1" Uncoated
WW00530-E1
Ø1/2" AR Coated for 2 - 5 µm
Please Wait
Wedged Window Selection Guide | |
---|---|
Wavelength Range | Substrate Material |
180 nm - 8.0 µm | Calcium Fluoride (CaF2) |
185 nm - 2.1 μm | UV Fused Silica |
200 nm - 5.0 µm | Sapphire |
200 nm - 6.0 µm | Magnesium Fluoride (MgF2) |
200 nm - 11 µm | Barium Fluoride (BaF2) |
250 nm - 1.6 µm | UV Fused Silica for 45° AOI |
350 nm - 2.0 μm | N-BK7 |
600 nm - 16 µm | Zinc Selenide (ZnSe) |
1.2 - 8.0 µm | Silicon (Si) |
2.0 - 16 µm | Germanium (Ge) |
V-Coated Wedged Windows |
特長
- 30 arcminウェッジウィンドウ
- Ø12.7 mm(Ø1/2インチ)およびØ25.4 mm(Ø1インチ)のウィンドウをご用意
- -E1の広帯域ARコーティング付き(2~5 µm)をご用意
- サイズのカスタム仕様にも対応(当社までお問い合わせください)
当社ではØ12.7 mm(Ø1/2インチ)およびØ25.4 mm(Ø1インチ)のARコーティング付きフッ化バリウム (BaF2)ウェッジウィンドウをご用意しています。ウェッジ付き光学素子はフリンジパターンの発生をなくし、また、面間における共振を防ぐのに役立ちます。ウィンドウはレーザ出力を外部の影響から保護でき、また、ビームサンプリングの用途で使用する際に便利です。 こちらのウィンドウはARコーティング付き(2~5 µm)でご用意しています。様々な基板材料やコーティングの平面ウィンドウもご用意しております。
フッ化バリウムの特性はフッ化カルシウム(CaF2)と似ていますが、高エネルギ放射に対して高い耐性を持つという利点があります。しかし、水に対する耐性はフッ化カルシウムよりも低くなります。フッ化バリウムは、水に触れると500 °Cで顕著な劣化が見られますが、乾燥した環境においては最高800 °Cにさらされる用途でも使用可能です。このウィンドウの結晶方位はランダムです。
フッ化バリウムの取扱いと安全性について
光学素子の取扱いには常に手袋をご着用ください。また、フッ化バリウム(BaF2)は素手で取り扱うと危険な材料なので、安全のため、フッ化バリウム取扱い時には手袋を着用し、取扱い後には入念に手を洗ってください。BaF2の製品安全データシート(MSDS)はPDF形式でこちらからダウンロードできます。
こちらでご紹介しているフッ化カルシウムウェッジウィンドウの他に、異なる基板材料を使用したウェッジウィンドウもご用意しております(右のセレクションガイドをご参照ください)。 一般的なレーザ波長域に対応したARコーティングを施したウェッジ付きレーザーウィンドウや、片面のみ広帯域ARコーティングを施したウェッジ付きビームサンプラもございます。 また、カスタム仕様のサイズや厚さでもご提供可能です。詳細は当社までお問い合わせください。
Posted Comments: | |
No Comments Posted |
Window Selection Guide (Table Sorted by Wavelength) | |||||
---|---|---|---|---|---|
Substrate and Window Type | Wavelength Range | Available AR Coatings | Reflectance over AR Coating Rangea | Transmission Data | Reflectance Data |
Calcium Fluoride (CaF2): Flat or Wedged | 180 nm - 8.0 μm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
UV Fused Silica: Flat, Wedged, V-Coated Flat, or V-Coated Wedged | 185 nm - 2.1 μm | Uncoated (Flat or Wedged) | - | Raw Data | - |
-UV Coating, 245 - 400 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C3 Coating, 261 - 266 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C6 Coating, 350 - 450 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-A Coating, 350 - 700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-B Coating, 650 - 1050 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C Coating, 1050 - 1700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
Sapphire: Flat or Wedged | 200 nm - 5.0 μm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0% at 0° AOI | Raw Data | Raw Data | ||
-E1 Coating, 2.0 - 5.0 µm | Ravg < 1.50%, Rabs < 3.0% (per Surface, 2.0 - 5.0 µm); Ravg < 1.75% (per Surface, 2.0 - 4.0 µm) at 0° AOI | Raw Data | Raw Data | ||
Magnesium Fluoride (MgF2): Flat or Wedged | 200 nm - 6.0 μm | Uncoated | - | Raw Data | - |
Barium Fluoride (BaF2): Flat or Wedged | 200 nm - 11 µm | Uncoated (Wedged Only) | - | Raw Data | - |
-E1 Coating, 2 - 5 µm | Ravg < 1.25%; Rabs < 2.5% at 0° AOI | Raw Data | Raw Data | ||
UV Fused Silica, for 45° AOI: Flat or Wedged | 250 nm - 1.6 µm | Coating for 250 nm - 450 nm | Ravg < 1.0% at 45° AOI | Raw Data | |
Coating for 350 nm - 1100 nm | Ravg < 2.0% at 45° AOI | Raw Data | |||
Coating for 400 nm - 700 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Coating for 600 nm - 1700 nm | Ravg < 1.5% at 45° AOI | Raw Data | |||
Coating for 700 nm - 1100 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Coating for 1200 nm - 1600 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Potassium Bromide (KBr): Flat | 250 nm - 26 µm | Uncoated | - | - | |
Infrasil®: Flat | 300 nm - 3 µm | Uncoated | - | Raw Data | - |
N-BK7: Flat, Wedged, V-Coated Flat, or V-Coated Wedged | 350 nm - 2.0 μm | Uncoated (Flat or Wedged) | - | Raw Data | - |
-A Coating, 350 - 700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C7 Coating, 400 - 700 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C10 Coating, 523 - 532 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C11 Coating, 610 - 860 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-B Coating, 650 - 1050 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C13 Coating, 700 - 1100 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
C14 Coating, 1047 - 1064 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C15 Coating, 523 - 532 nm & 1047 - 1064 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C Coating, 1050 - 1700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
Zinc Selenide (ZnSe): Flat or Wedged | 600 nm - 16 µm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-E4 Coating, 2 - 13 µm (Only Flat) | Ravg < 3.5%; Rabs < 6% at 0° AOI | Raw Data | Raw Data | ||
-E2 Coating, 4.5 - 7.5 µm (Only Flat) | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-E3 Coating, 7 - 12 µm (Only Wedged) | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-G Coating, 7 - 12 µm (Only Flat) | Ravg < 1% at 0° AOI | Raw Data | Raw Data | ||
Silicon (Si): Flat or Wedged | 1.2 - 8.0 μm | Uncoated | - | Raw Data | - |
-E1 Coating, 2 - 5 µm (Only Wedged) | Ravg < 1.25%; Rabs < 2.5% at 0° AOI | Raw Data | Raw Data | ||
-E Coating, 3 - 5 µm (Only Flat) | Ravg < 2% at 0° AOI | Raw Data | Raw Data | ||
Germanium (Ge): Flat or Wedged | 1.9 - 16 μm | Uncoated, 2.0 - 16 μm | - | Raw Data | - |
-C9 Coating, 1.9 - 6 µm (Only Flat) | Ravg < 2% at 0° AOI | Raw Data | Raw Data | ||
-E3 Coating, 7 - 12 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data |
Item # | WW00530-E1 | WW01050-E1 |
---|---|---|
Wedge Angle | 30 ± 10 arcmin | |
Diameter | 1/2" (12.7 mm) | 1" (25.4 mm) |
Diameter Tolerance | +0.0 / -0.2 mm | |
Thickness | 3.0 mm | 5.0 mm |
Thickness Tolerance | ±0.1 mm | |
Clear Aperture | > Ø11.4 mm | ≥Ø22.9 mm |
Surface Flatnessa | ≤λ/8 Over Central Ø5 mm ≤λ/4 Over Entire Clear Aperture | ≤λ/8 Over Central Ø10 mm ≤λ/4 Over Entire Clear Aperture |
Surface Quality | 40-20 Scratch-Dig | |
AR Coating Range | 2 µm - 5 µm (-E1 Coating) | |
Reflectance over AR Coating Rangeb | Ravg < 1.25% (per Surface) Rabs < 2.5% (per Surface) Both Sides are Coated | |
Transmission over AR Coating Rangeb | Tavg > 94% Tabs > 92% | |
Reflectance Data (Click for Graph) | Raw Data | |
Substrate | Barium Fluoridec | |
Transmission Data (Click for Graph) | Raw Data |